Assessing the impact of loss mechanisms in solar cell candidate
In a new paper published in EPJ Plus, Maykel Courel from the Centro Universitario de los Valles (CUValles), Universidad de Guadalajara, Mexico, and co-authors, look at the limitations of the material antimony sulfide selenide, which has emerged as a potential candidate for solar cell fabrication.
A semiconductor, antimony sulfide selenide has been intensively studied by researchers working on thin-film solar cells, due to the fact that direct optical transitions result in the material possessing a high absorption coefficient. The material’s application to devices that convert light into electricity using semiconducting materials is still in its early days, however.
Currently, the efficiency of this material is at a maximum of around 10 percent, well below 29 percent, the maximum efficiency expected for this type of technology.
The researchers set about testing the limiting factors that are affecting this efficiency, focusing on the effect of loss mechanisms on antimony sulfide selenide cells using an analytical model.
The team found that for typical parameters chosen for their simulations, electron-hole recombination in a substrate — known as bulk recombination — and interface recombination which happens when two semiconductor bandgaps have a staggered shape, are the main problems that degrade the device performance.
They suggest that materials scientists working on either the reduction in defects at interface or defects at bulk in antimony sulfide selenide devices would not be able to obtain efficiencies greater than 10 percent. On the other hand, with a carrier lifetime longer than 100 nanoseconds with a recombination speed lower than 1 centimetre per second efficiencies for such technology could top 14 percent.